Crafts

Micaceous paste Micaceous paste from the “Apache” tradition. This formula, conceived thanks to the collaboration of the New Mexico ceramist, Felipe Ortega, recreates the original composition of clays used by the Apache tradition to make utilitarian ceramics for direct fire use. It is composed of red clays with a low coefficient of expansion and, above all, an abundant matrix of mica, which gives it elasticity and gives it a very recognizable finish. Its original character is obtained by cooking with firewood. Available in extruded plastic paste. Amount: 12.5kg Cooking temperature: 920-1000ºC Humidity: 22% Plasticity (IP Atterberg): 24 Calcimetry (CaCO3): 0% Drying shrinkage: 5.8% Cooking shrinkage (950ºC): 0.3% Porosity (water absorption 950ºC): 12.9% Dry mechanical strength: 5.9 N/mm2 Mechanical strength fired (950ºC): 19.5 N/mm2 Expansion coefficient (25-500ºC): 58.8x10^-7ºC^-1 Reference 102300010000

Porcelana con fibra de papel Cellulain® es una porcelana blanca traslúcida con fibra de papel que destaca por su excepcional plasticidad, lo que la hace única para el modelado. Está especialmente diseñada para la creación en porcelana de formas imposibles. La presencia de fibras de papel en su interior evita la formación de grietas y deformaciones, convirtiéndola en un medio de expresión artística muy particular. Su fórmula es muy estable y permite un rango de cocción seguro entre 1230 y 1270ºC. Disponible en pasta plástica extrusionada. Se presenta en un práctico formato cilíndrico de 5kg con doble envase. Temperatura de cocción: 1230-1270ºC Temperatura bizcocho: 1000ºC Humedad: 26% Plasticidad (IP Atterberg): 11 Calcimetría (CaCO3): 0% Contracción secado: 4.4% Contracción cocción (1250ºC): 11.4% Porosidad (absorción de agua 1250ºC): 2.8% Resistencia mecánica en seco: 4.5 N/mm2 Resistencia mecánica cocido (1250ºC): 21.0 N/mm2 Coeficiente dilatación (25-500ºC): 58.8x10-7ºC-1 Reference 163000010000

Pasta azul. Destaca por su apreciado color azul a baja temperatura y atmósfera oxidante. Presenta una gran finura y plasticidad que le ofrece unas magníficas prestaciones para tornear y modelar. Muy buen comportamiento con esmaltes. Disponible en pasta plástica extrusionada. Cantidad: 5kg Cooking temperature: 1050-1080ºC Humedad (torno): 19% Plasticidad (IP Atterberg): 15 Calcimetría (CaCO3): 16% Contracción secado: 5.6% Contracción cocción (1050ºC): -0.3% Porosidad (absorción de agua 1050ºC): 12.1% Resistencia mecánica en seco: 4.1 N/mm2 Resistencia mecánica cocido (1050ºC): 31.7 N/mm2 Coeficiente dilatación (25-500ºC): 76.6x10^-7ºC^-1

Pasta refractaria gris con 40% chamota media 0-1.5 mm. Diseñada para cerámica artística y decorativa, es ideal para esculturas de mayor tamaño y piezas grandes de exterior. El elevado contenido en chamota confiere carácter a la pieza cerámica y le proporciona un excelente comportamiento durante el secado y la cocción. En función de la temperatura de cocción, desarrolla una bella gama de grises, desde el tono cemento al gris oscuro, que satisface las tendencias más vanguardistas en cerámica artística y decorativa. Disponible en pasta plástica extrusionada. Cantidad: 12.5kg Cooking temperature: 1200-1300ºC Temperatura bizcocho: 1000ºC Humedad: 17% Plasticidad (IP Atterberg): 16 Calcimetría (CaCO3): 0% Contracción secado: 4.5% Contracción cocción (1300ºC): 3.9% Porosidad (absorción de agua 1300ºC): 4.5% Resistencia mecánica en seco: 2.3 N/mm2 Resistencia mecánica cocido (1300ºC): 21.1 N/mm2 Coeficiente dilatación (25-500ºC): 57.5x10^-7ºC^-1 Reference 145300010000