SIO-2 modeling and sculpture set
PT/CHF chamotte terracotta paste 0-0.5mm
PT/CHF chamotte terracotta paste 0-0.5 mm 12.5kg.
Terracotta paste chamotte with 0-0.5 mm fine chamotte 25%. Ideal for medium sized pieces. The presence of chamotte gives it a textured surface (not smooth) that gives it character and, in turn, provides it with ideal properties for the production of pieces that are difficult to dry, avoiding deformations and the appearance of cracks. Its high resistance to frost and environmental degradation make it ideal for pieces exposed to the outside (large planters, tiles, roof tiles, etc.). Available in extruded plastic paste, suitable for modeling and molding. Cooking temperature: 990-1085ºC
Humidity (lathe): 19% Plasticity (IP Atterberg): 13 Calcimetry (CaCO3): 14% Drying shrinkage: 5.6% Cooking shrinkage (1000ºC): 0.1% Porosity (water absorption 1000ºC): 15.5% Dry mechanical strength: 5.7 N/ mm2 Fired mechanical strength (1000ºC): 18.9 N/mm2 Expansion coefficient (25-500ºC): 69.4x10^-7ºC^-1
Ref.10 720 001 | EAN8422830107025
Pasta PGV gres culinario Sio-2
Pasta de gres culinario 12.5 kg
Pasta de gres culinario. Su fórmula especial está concebida para la realización de piezas para vajilla de alta resistencia al impacto. Gresifica a media temperatura (semigres). El color blanco en cocción proporciona la base excelente para el desarrollo de color en esmaltes y óxidos colorantes, siendo una pasta muy adecuada para múltiples aplicaciones. Su fina textura la hacen ideal para tornear y modelar. Disponible en pasta plástica.
Temperatura de cocción: 1150-1180ºC
Humedad: 20%
Plasticidad (IP Atterberg): 14
Calcimetría (CaCO3): 0%
Contracción secado: 5.3%
Contracción cocción (1180ºC): 6.1%
Porosidad (absorción de agua 1180ºC): 0.1%
Resistencia mecánica en seco: 6.9 N/mm2
Resistencia mecánica cocido (1180ºC): 38.1 N/mm2
Coeficiente dilatación (25-500ºC): 61.4x10^-7ºC^-1
Ref.11 800 001 | EAN8422830118014
Pasta PLV verde Sio-2
Pasta verde PLV 5kg.
Pasta verde Sio-2. Destaca por su apreciado color verde a baja temperatura y atmósfera oxidante. Presenta una gran finura y plasticidad que le ofrece unas magníficas prestaciones para tornear y modelar. Muy buen comportamiento con esmaltes. Disponible en pasta plástica extrusionada.
Temperatura de cocción: 1050-1080ºC
Humedad (torno): 19%
Plasticidad (IP Atterberg): 15
Calcimetría (CaCO3): 16%
Contracción secado: 5.3%
Contracción cocción (1050ºC): -0.1%
Porosidad (absorción de agua 1050ºC): 11.2%
Resistencia mecánica en seco: 4.2 N/mm2
Resistencia mecánica cocido (1050ºC): 28.7 N/mm2
Coeficiente dilatación (25-500ºC): 77.2x10^-7ºC^-1
Ref.10 500 010 | EAN8422830105021
Flumo Sio-2 Plus 1 lt
Slip (liquid clay) without cooking, which dries in the air acquiring great hardness. It is used with plaster molds through the traditional casting system, obtaining a piece of high quality and ceramic resistance. Once dry, it can be polished, painted and varnished. The product can also be colored when it is still in a liquid state. Suitable for children's use and in accordance with European regulations EN-71 and USA AP regulations, a non-toxic product. Quantity: 1 lt
Red PF paste 12.5 kg
Pasta PF roja tradicional de alfarería de alta calidad.
Pasta muy polivalente y apreciada por su finura, plasticidad y regularidad. Presenta unos coeficientes de dilatación idóneos para los esmaltes estándares de alfarería, tanto en mono como en bicocción. A destacar sus magníficos resultados en atmósfera reductora (técnica de reflejos metálicos). Disponible en polvo y en pasta plástica extrusionada con diferentes humedades para su aplicación en los distintos procesos de conformado: torneado, modelado y moldeado (extrusión y prensado).
Cooking temperature: 970-1055ºC Humedad (torno): 22% Plasticidad (IP Atterberg): 17 Calcimetría (CaCO3): 10% Contracción secado: 5.5% Contracción cocción (1000ºC): 0.6% Porosidad (absorción de agua 1000ºC): 13.5% Resistencia mecánica en seco: 6.6 N/mm2 Resistencia mecánica cocido (1000ºC): 27.9 N/mm2 Coeficiente dilatación (25-500ºC): 77.7x10^-7ºC^-1
JADE porcelana imperial translucida
Porcelana imperial translúcida
Jade es una porcelana super translúcida procedente de la ciudad de Jingdezhen, capital mundial de la porcelana y cuna de la porcelana imperial china desde hace 1.700 años. Se caracteriza por su extraordinaria translucidez y blancura. Es ideal para porcelana decorativa y vajilla. Disponible en pasta plástica extrusionada. Se presenta en un práctico formato cilíndrico de 5 kg con doble envase.
Temperatura de cocción: 1260-1290ºC
Temperatura bizcocho: 1000ºC
Humedad: 25%
Plasticidad (IP Atterberg): 9
Calcimetría (CaCO3): 0%
Contracción secado: 5.9%
Contracción cocción (1270ºC): 10.2%
Porosidad (absorción de agua 1270ºC): 0.0%
Resistencia mecánica en seco: 2.4 N/mm2
Resistencia mecánica cocido (1270ºC): 44.0 N/mm2
Coeficiente dilatación (25-500ºC): 66x10^-7ºC^-1
166000010000
APACHE micaceous paste Sio-2
Micaceous paste
Micaceous paste from the “Apache” tradition. This formula, conceived thanks to the collaboration of the New Mexico ceramist, Felipe Ortega, recreates the original composition of clays used by the Apache tradition to make utilitarian ceramics for direct fire use. It is composed of red clays with a low coefficient of expansion and, above all, an abundant matrix of mica, which gives it elasticity and gives it a very recognizable finish. Its original character is obtained by cooking with firewood. Available in extruded plastic paste. Amount: 12.5kg
Cooking temperature: 920-1000ºC
Humidity: 22% Plasticity (IP Atterberg): 24 Calcimetry (CaCO3): 0% Drying shrinkage: 5.8% Cooking shrinkage (950ºC): 0.3% Porosity (water absorption 950ºC): 12.9% Dry mechanical strength: 5.9 N/mm2 Mechanical strength fired (950ºC): 19.5 N/mm2 Expansion coefficient (25-500ºC): 58.8x10^-7ºC^-1
102300010000
CELLULAIN porcelana con fibra de papel Sio-2
Porcelana con fibra de papel
Cellulain® es una porcelana blanca traslúcida con fibra de papel que destaca por su excepcional plasticidad, lo que la hace única para el modelado. Está especialmente diseñada para la creación en porcelana de formas imposibles. La presencia de fibras de papel en su interior evita la formación de grietas y deformaciones, convirtiéndola en un medio de expresión artística muy particular. Su fórmula es muy estable y permite un rango de cocción seguro entre 1230 y 1270ºC. Disponible en pasta plástica extrusionada.
Se presenta en un práctico formato cilíndrico de 5kg con doble envase.
Temperatura de cocción: 1230-1270ºC
Temperatura bizcocho: 1000ºC
Humedad: 26%
Plasticidad (IP Atterberg): 11
Calcimetría (CaCO3): 0%
Contracción secado: 4.4%
Contracción cocción (1250ºC): 11.4%
Porosidad (absorción de agua 1250ºC): 2.8%
Resistencia mecánica en seco: 4.5 N/mm2
Resistencia mecánica cocido (1250ºC): 21.0 N/mm2
Coeficiente dilatación (25-500ºC): 58.8x10-7ºC-1
163000010000
ALETSCH porcelana moloquita Sio-2
Porcelana con moloquita
Aletsch es una porcelana blanca con 20% de chamota 0.2-0.5 mm de moloquita. La moloquita confiere a la porcelana una textura muy particular y le proporciona un excelente comportamiento durante el secado y la cocción. Su fórmula es muy estable y permite un rango de cocción seguro entre 1230 y 1270 °C. Disponible en pasta plástica extrusionada.
Se presenta en un práctico formato cilíndrico de 5kg con doble envase.
Temperatura de cocción: 1230-1270ºC
Temperatura bizcocho: 1000ºC
Humedad: 20%
Plasticidad (IP Atterberg): 8
Calcimetría (CaCO3): 0%
Contracción secado: 4.0%
Contracción cocción (1250ºC): 7.7%
Porosidad (absorción de agua 1250ºC): 0.2%
Resistencia mecánica en seco: 1.6 N/mm2
Resistencia mecánica cocido (1250ºC): 22.5 N/mm2
Coeficiente dilatación (25-500ºC): 52.7x10^-7ºC^-1